How to Improve the Adhesion of Neoprene Glue to Glass Fiber Cloth?

Views : 251
Author : Heaterk
Update time : 2022-07-28 16:05:05

Neoprene-coated fiberglass fabric is a commonly used coating composite material in the industry. This material has excellent high and low-temperature resistance and is waterproof, oil-proof, ozone-resistant, and anti-aging, so it is widely used in various industries.

Then in the production process of neoprene, the adhesion of the butadiene rubber glue to the glass fiber cloth significantly influences the product's quality. Heaterk provides some suggestions based on years of manufacturing experience; hoping to help you.

Neoprene coating process

The peel strength of the neoprene adhesive is related to the formula, process, and usage. The available neoprene adhesive needs to add tert-butyl phenolic resin to improve the adhesion to complex and dense adherents such as metal, glass, thermosetting plastics, etc. As the amount of resin increases, the peel strength increases, but when the amount of resin exceeds 45 parts (CR is 100 parts), the peel strength decreases instead. Therefore, too small or too little amount of 2402 resin will make the peel strength lower.

After the chloroprene rubber is mixed, the relative molecular weight is reduced, the viscosity of the glue is small, and the wettability is good, which can improve the peel strength.

When the neoprene adhesive is used to bond non-porous adherents, the drying time after gluing should not be too short. Otherwise, the solvent will be wrapped after lamination, and the peel strength will be reduced. In addition, it should be compacted and smashed after lamination to drive out the air. Otherwise, the peel strength will be reduced. The outstanding feature of neoprene adhesive is the high initial strength, but it takes 5~7 days to reach the maximum power. Allow enough time for actual use and evaluation of management.

In short, to increase the peel strength of the neoprene adhesive, a certain amount of 2402 resin should be added. It is appropriate to use 40~50 parts. The neoprene rubber should be adequately mixed to make the glue have good wettability. 100 parts of hydroxyl CRAF, 45 pieces of tert-butyl phenolic resin, five pieces of light magnesium oxide, 165 pieces of toluene, acetic acid Neoprene adhesive prepared with 165 pieces of ethyl ester and 165 parts of n-hexane, its peel strength is 1.15K.m-1

Get in touch with the experts at Heaterk to discuss more expertise in coated fiberglass fabrics

  

Related News
Read More >>
High Silica Fabric: Unlocking the Potential in Diverse Industries High Silica Fabric: Unlocking the Potential in Diverse Industries
Mar .30.2023
High silica fabric, a versatile material known for its unique combination of properties, has seen increased adoption across a wide range of industries. This article explores the various application fields of high silica fabric, highlighting its benefits and potential future developments.
Application of Glass Fiber Needle Mat Application of Glass Fiber Needle Mat
Mar .22.2023
Fiberglass needle mat, also known as fiberglass insulation mat or needled fiberglass mat, is a nonwoven material made by mechanically bonding randomly guide glass fibers. It has numerous applications due to its unique properties, such as high-temperature resistance, thermal insulation, noise reduction, and low thermal conductivity.
Fiberglass Mat VS Cloth Fiberglass Mat VS Cloth
Mar .10.2023
Fiberglass is a composite material consisting of extruded glass strands. The fiberglass used in the automotive industry, shipbuilding, and hull repair differs from the fiberglass used for insulation.
Celebrating Arthur's Birthday Celebrating Arthur's Birthday
Feb .03.2023
Today is Heaterk's employee Arthur's birthday, and Heaterk held a birthday party for Arthur.
Arthur is the operations director of Heaterk. Today is also the sixth year he has joined the Heaterk family. During these six years, Arthur has witnessed Heaterk grow step by step from a traditional company to a professional international manufacturer of professional fireproof insulation materials. .